    Preparation and characterization of a thin-film composite reverse osmosis membrane using a polysulfone membrane including metal-organic frameworks

    Year: 2017

    Journal: J. Membr. Sci., Volume 541, NOV 1, page 510–518

    Authors: Park, Hee Min; Jee, Ki Yong; Lee, Yong Taek

    Organizations: Industrial Fundamental Technology Development Program - Ministry of Trade, Industry & Energy (MOTIE, KOREA) [10050503]

    Keywords: Thin-film composite reverse osmosis membrane; Interfacial polymerization; Metal-organic frameworks; Polysulfone

    The objectives of this paper were to elucidate the performance of a thin-film composite (TFC) reverse osmosis (RO) membrane by modifying the support layer. In order to improve the hydrophilicity and porosity of the support layer, we prepared a polysulfone (PSf) membrane containing an HKUST-1 [Cu-3(BCT2)] metal organic framework (MOF) treated with sulfuric acid for the stability of water. N, N-dimethylformamide (DMF)/water was used as the solvent/non-solvent pair, and the TFC RO membrane was formed by the interfacial polymerization of m-phenylene diamine (MPD) in aqueous solution with trimesoyl chloride (TMC) in organic solution on the MOF/PSF support layer. The optimized concentration of MPD-TMC was investigated through XPS, and the manufactured membrane had a thin, smooth film when paired with a hydrophilic and porous support layer. The active layer thickness of novel membrane was 0.029 mu m via FTIR analysis that the thickness compared to a commercial RO membrane having a thickness of 0.2 mu m. Also, the novel membrane showed improved flux and fouling resistance compared to the TFC RO membrane with a PSF support layer, without altering the salt rejection property.