    Colloidal PTFE dispersion in commercial engine oil: Lubrication by Pluronic adsorption at the interface

    Year: 2020

    Journal: Colloid Surf. A-Physicochem. Eng. Asp., Volume 597, JUL 20

    Authors: Shah, Vidhi; Panchal, Tirth; Bharatiya, Bhavesh; Patel, Nimeshchandra S.; Shukla, Atindra D.; Shah, Dinesh O.

    Organizations: Department of Science and Technology (DST), New Delhi, IndiaDepartment of Science & Technology (India) [SB/FT/CS-080/2013]

    Keywords: lubricant; coefficient of friction; dispersion stability; PTFE; tribometer; Pluronics

    PTFE particles with an average size of similar to 300 nm were dispersed in20w40 commercial engine oil using Pluronic (R) surfactant. The role of series of different Pluronics with varying molecular weight and HLB was investigated. The dispersion stability was checked by UV-Vis-NIR spectrophotometer and by force transducer. The result indicates significant dispersion stability for low molecular weight and low HLB Pluronic, attributed to faster diffusion at PTFE-oil interface and resultant steric stability. L92 based formulation with less than 10% sedimentation even after 48 hrs, was evaluated for further tribological tests, i.e. wear, friction and pressure profile. Hydrodynamic oil film pressure profile using journal bearing showed significant increase in the load carrying capacity owing to PTFE dispersion in engine oil. Four ball tester depicted decreases in wear scar diameter for L-92 stabilised dispersion. Plausible molecular mechanism is proposed based on adsorption of polymers bilayer around PTFE particles through tail-tail interactions between PEO chains.