    Degradation of Polypropylene and Jute Fiber-Reinforced Composites Exposed to Natural and Accelerated Aging: Mechanical Properties and Wettability

    Year: 2021

    Journal: Chemistry-Switz., Volume 3, DEC, page 1392–1400

    Authors: Sanvezzo, Paula Bertolino; Negreiros, Fernanda Pereira de Castro; Branciforti, Marcia Cristina

    Keywords: accelerated weathering; natural weathering; recycling; industrial waste; natural fiber; infrared spectroscopy

    Population growth and the way resources are being exploited are directly affecting the environment. The natural fiber market, for example, is worth billions of dollars and a huge amount of the fibers becomes waste. This considerable amount of waste motivates the study of the fibers as a reinforcement in polymeric matrix, which benefits both the environmental sustainability and technical-commercial development of new materials with good properties and reduced cost. In this study, jute fiber-reinforced composites previously manufactured from an industrial waste (W), polypropylene, compatibilizer, and nano-calcium carbonate (N), were exposed to natural and accelerated aging. The composites were tested by infrared spectroscopy, contact angle (CA) measurement, and tensile test. Infrared analysis showed greater oxidative degradation after accelerated aging. All CA values continued above 90 degrees after natural aging. Among all compositions, the ones with the presence of N had the highest CA values, showing that N acted as a waterproofing agent. After accelerated aging, a significant decrease in all CA values was observed. The composites did not show significant variation in the elastic modulus after either aging. Deformation at break decreased significantly for compositions with no jute fiber in both aging programs. No remarkable reduction was observed in the compositions with jute fibers.
    View publication