    Effects of Electron Beam Irradiation on the Mechanical, Thermal, and Surface Properties of Some EPDM/Butyl Rubber Composites

    Year: 2018

    Journal: Polymers, Volume 10, NOV

    Authors: Stelescu, Maria Daniela; Airinei, Anton; Manaila, Elena; Craciun, Gabriela; Fifere, Nicusor; Varganici, Cristian; Pamfil, Daniela; Doroftei, Florica

    Organizations: Research and Innovation Ministry, RDI Programme for Space Technology and Advanced Research-STAR-ROSA [140/2017]

    Keywords: EPDM; electron beam irradiation; butyl rubbers; mechanical properties; thermal stability; crosslinking; contact angle

    The effects of electron beam irradiation on the properties of ethylene propylene diene monomer (EPDM)/butyl rubber composites in presence of a polyfunctional monomer were investigated by means of differential scanning calorimetry (DSC), thermal analysis, scanning electron microscopy (SEM), attenuated total reflection absorption infrared spectroscopy (ATR-IR), and mechanical and surface energy measurements. The samples were exposed over a wide range of irradiation doses (20-150 kGy). The EPDM matrix was modified with butyl rubber, chlorobutyl rubber, and bromobutyl rubber. The gel content and crosslink density were found to increase with the electron beam irradiation dose. The values of the hardness and modulus increased gradually with the irradiation dose, while the tensile strength and elongation at break decreased with increasing irradiation dose. The EPDM/butyl rubber composites presented a higher thermal stability compared to the initial EPDM sample. The incorporation of butyl rubbers into the EPDM matrix led to an increase in material hydrophobicity. A similar trend was observed when the irradiation dose increased. The greatest change in the surface free energy and the contact angles occurs at an irradiation dose of 20 kGy. The Charlesby-Pinner plots prove the tendency to crosslinking as the irradiation dose increases.