    Fabrication and Testing of Multi-Hierarchical Porous Scaffolds Designed for Bone Regeneration via Additive Manufacturing Processes

    Year: 2022

    Journal: Polymers, Volume 14, OCT

    Authors: Gonzalez-Henriquez, Carmen M.; Rodriguez-Umanzor, Fernando E.; Acuna-Ruiz, Nicolas F.; Vera-Rojas, Gloria E.; Terraza-Inostroza, Claudio; Cohn-Inostroza, Nicolas A.; Utrera, Andres; Sarabia-Vallejos, Mauricio A.; Rodriguez-Hernandez, Juan

    Organizations: FONDECYT [1170209, 1220251, 1200329]; Universidad San Sebastian (USS) [VRID FAI 21/17]; Ministerio de Ciencia, Innovacion y Universidades [RTI2018-096328-B-I00]; PTI + SUSPLAST from CSIC; ANID through FONDEQUIP [EQM 130028]; VRAC of Universidad Tecnologica Metropolitana [LPR20-03, L318-02]; Ministerio de Ciencia, Innovacion y Universidades (FONDOS FEDER) [MAT2016-78437-R]; PIT FAB3D; PTI + Salud Global

    Keywords: bone scaffold; additive manufacturing; salt leaching; wrinkled micropatterns; ATRP synthesis

    Bone implants or replacements are very scarce due to the low donor availability and the high rate of body rejection. For this reason, tissue engineering strategies have been developed as alternative solutions to this problem. This research sought to create a cellular scaffold with an intricate and complex network of interconnected pores and microchannels using salt leaching and additive manufacturing (3D printing) methods that mimic the hierarchical internal structure of the bone. A biocompatible hydrogel film (based on poly-ethylene glycol) was used to cover the surface of different polymeric scaffolds. This thin film was then exposed to various stimuli to spontaneously form wrinkled micropatterns, with the aim of increasing the contact area and the material's biocompatibility. The main innovation of this study was to include these wrinkled micropatterns on the surface of the scaffold by taking advantage of thin polymer film surface instabilities. On the other hand, salt and nano-hydroxyapatite (nHA) particles were included in the polymeric matrix to create a modified filament for 3D printing. The printed part was leached to eliminate porogen particles, leaving homogenously distributed pores on the structure. The pores have a mean size of 26.4 +/- 9.9 mu m, resulting in a global scaffold porosity of similar to 42% (including pores and microchannels). The presence of nHA particles, which display a homogeneous distribution according to the FE-SEM and EDX results, have a slight influence on the mechanical resistance of the material, but incredibly, despite being a bioactive compound for bone cells, did not show a significant increase in cell viability on the scaffold surface. However, the synergistic effect between the presence of the hydrogel and the pores on the material does produce an increase in cell viability compared to the control sample and the bare PCL material.