    Hydrophilicity and flux properties improvement of high performance polysulfone membranes via sulfonation and blending with Poly(lactic acid)

    Year: 2022

    Journal: High Perform. Polym., Volume 34, DEC, page 1115–1130

    Authors: Tasci, Reyhan O.; Kaya, Mehmet A.; Celebi, Mithat

    Organizations: TUBITAK [1003, 113Y370]; Yalova University [BAP 2015/YL/058]

    Keywords: Polysulfone; poly(lactic acid); sulfonation; blend; membrane; hydrophilicity

    To achieve increased flow and reduce fouling, polymeric membranes can be functionalized with hydrophilic groups such as sulfone, amines, and others. This research has aimed at the sulfonation of Polysulfone (PSU) with various agents and at varying substitution degrees to change its hydrophobic character. PSU was also blended with Poly(lactic acid) (PLA), which is a more hydrophilic polymer. The phase inversion method was used to make PSU, PLA, sulfonated PSU, and PSU/PLA blend-based membranes. Sulfonation degrees of sulfonated PSU membranes were assessed using FT-IR, mechanical characteristics of membranes were determined, and thermal properties of membranes were clarified using DSC and TGA techniques. Hydrophilic natures and membrane alterations were investigated, as well as contact angle and water uptake measures. Among three distinct sulfonation agents (trimethylsilyl chlorosulfonate (TMSCS), sulfuric acid, and chlorosulfonic acid) employed to produce a 20% sulfonation degree of polysulfone, TMSCS was chosen as having the highest sulfonation efficiency (91.5%). With increasing sulfonation degree, a drop in molecular weight was seen in all sulfonated polysulfone samples. The mechanical strength values of polysulfone after sulfonation with TMSCS rose from 35.23 MPa to 63.35 MPa, while the contact angle value decreased from 85.58 degrees to 71 degrees. The contact angle value reduced from 85.58 degrees to 64.68 degrees while the mechanical strength of the PSU and PSU/PLA (50:50) blend increased from 35.23 MPa to 39.3 MPa. Membranes were also tested for pure water flux, hydrostability, and biostability. In terms of application requirements, it was determined that sulfonated PSU-based membranes manufactured with TMSCS with a 20% sulfonation degree and PSU/PLA blend-based membranes with a 50:50 (w:w) ratio have the optimum compositions with high flux quantities.