    Mapping Depletion of Lubricant Films on Antibiofouling Wrinkled Slippery Surfaces

    Year: 2018

    Journal: ACS Appl. Mater. Interfaces, Volume 10, OCT 3, page 33669–33677

    Authors: Peppou-Chapman, Sam; Neto, Chiara

    Organizations: Australian Government Research Training Program (RTP) scholarship; University of Sydney Nano Institute Top-Up Scholarship

    Keywords: SLIPS; slippery surfaces; immobilized liquid; AFM; force mapping; thin films; biofouling; silicone oil; Teflon

    Slippery liquid infused porous surfaces (SLIPS) have recently gained a lot of attention because of their wide range of applications. We recently showed that SLIPS with most of their surface depleted of lubricant, as little lubricant as 0.02 +/- 0.01 mu L cm(-1), were effective against marine biofouling. Characterization of the depletion and configuration of the immobilized liquid layer on SLIPS is crucial to optimizing their performance. Previous attempts at mapping lubricant thickness have been diffraction limited or indirectly measured thickness. Here, we use atomic force microscopy meniscus force measurements to directly map lubricant thickness with nanoscale resolution on wrinkled surfaces made from Teflon and poly(4-vinylpyridine) (P4VP). Using this method, we show that SLIPS are easily depleted and are effectively heterogeneous surfaces, where the majority of the surface is a thick lubricating layer stabilized by capillary forces and part nanothin layer stabilized long-range intermolecular forces. We found that the depleted silicone oil thickness on the tops of nonwettable (Teflon) wrinkles is approx. 5 nm, close to but greater than the minimum measurable thickness of approx. 3 nm. The silicone oil thickness on the tops of wettable (P4VP) wrinkles is approx. 15 nm. Surfaces in this state still show antibiofouling properties and thus show that a thick lubricating layer is not necessary for all favorable properties of SLIPS.