    Microporous carbon from fullerene impregnated porous aromatic frameworks for improving the desalination performance of thin film composite forward osmosis membranes

    Year: 2018

    Journal: J. Mater. Chem. A, Volume 6, JUN 28, page 11327–11336

    Authors: Wu, Xing; Shaibani, Mandokht; Smith, Stefan J. D.; Konstas, Kristina; Hill, Matthew R.; Wang, Huanting; Zhang, Kaisong; Xie, Zongli

    Organizations: CSIRO Manufacturing; Bureau Frontier Sciences and Education [QYZDB-SSW-DQC044]; Bureau of International Cooperation [132C35KYSB20160018]; Chinese Academy of Sciences; CAS; CSIRO; China Scholarship Council

    Porous additives and polymer modifications are becoming increasingly common routes to address some of the current challenges faced by membrane technologies. Here, using carbonization and pre-impregnation of fullerene to enhance the performance of a porous aromatic framework, we have developed a novel hydrophobic porous membrane additive (C-60@PAF(900)) for enhancing the performance of forward osmosis (FO) water purification membranes. We examined the influence of C-60@PAF(900) loading on the polyamide (PA) layer in the fabrication of novel thin film nanocomposite (TFN) FO membranes and subsequently investigated the desalination performance of the resulting TFN FO membranes. The results showed that the addition of nanoporous C-60@PAF(900) greatly enhanced the water flux and water permeability of TFN FO membranes. Using 2 mol L-1 NaCl as the draw solution and 10 mmol L-1 NaCl as the feed solution, adding 0.01 w/v% C-60@PAF(900) into the FO membrane increased the water flux from 7.4 LMH to 12.4 LMH in the ALFS mode (active layer facing the feed solution) and from 12.6 LMH to 21.3 LMH in the ALDS mode (active layer facing the draw solution). To understand these results, the effect of C-60@PAF(900) on the surface morphology and chemistry of TFN FO was also investigated. Compared to the pristine FO membranes, the TFN FO membranes possessed a less dense crosslinked network due to the influence of C-60@PAF(900) on the interfacial polymerization process, and the interfacial repulsion between C-60@PAF(900) and polyamide. Together, this study provides an insight into the performance and potential effects of C-60@PAF(900) on advanced TFN FO membranes.