    Silica-based hybrids for adhesive coatings and their anti-salt damage in the protection of ancient sandstone

    Year: 2021

    Journal: Prog. Org. Coat., Volume 151, FEB

    Authors: Jia, Mengjun; He, Ling; Pan, Aizhao; Ma, Xiaoqin; Huang, Shengying; Simon, Stefan

    Organizations: National Key Research and Development Project [2019YFC1520504]; National Natural Science Foundation of China (NSFC) [51873173, 51573145]; China Scholarship Council (CSC)

    Keywords: Silica-based hybrid; Adhesive coatings; Salt damage; Crystallization pattern; Sandstone protection

    Hybrid coatings have been used as the protective materials on sandstone monuments for many decades. But the protective performance is strongly depended on the adhered interface between protective coating and matrix. To find out how the hybrid coatings affect the adhesive performances and anti-salt damage behaviors during Na2SO4 salt-loaded hygrothermal aging (SLHA) cycles, the surface/mechanical properties of three silica-based hybrid coatings (S1-S3) and their anti-salt damage results (surface weathering appearance, mass change, porosity, water absorption and morphology of pore structures) of the sandstones adhered by these hybrid coatings have been evaluated and discussed. The results reveal that dendritic Na2SO4 crystals cover on the sand grains in both natural and hydrophilic silica/PVA (S1) adhered sandstones, which makes the adhered sandstone perform the least damage. Owing to the high adhesive and mechanical strength, S1-adhered sandstones perform the best anti salt damage during Na2SO4 SLHA cycles. While the needle-like and cumulate ellipsoidal Na2SO4 crystals precipitate in the pores and interstices result to much severe salt damaged in adhered sandstones by hydrophobic P (GMA-MAPOSS) (S2) and PGMA-g-P(MA-POSS) (S3) during Na2SO4 SLHA cycles, although they enhanced the strength of adhesive pore walls. Actually, the macro salt damage behaviors on the sandstones treated by different hybrid coatings are proved to be a competition result of different crystallization patterns. Therefore, the pore interface adjusted by protective coatings should be one of the decisive factors for anti-salt damage during the sandstone protection.