    Suppressing the Hofmeister Anion Effect by Thermal Annealing of Thin-Film Multilayers Made of Weak Polyelectrolytes

    Year: 2022

    Journal: Macromolecules, Volume 55, NOV 8, page 9571–9582

    Authors: Klacic, Tin; Bohinc, Klemen; Kovacevic, Davor

    Organizations: Croatian Science Foundation [IPS-2020-01-6126]; Slovenian Research Agency [P3-0388, J7-2595]; CEEPUS [CIII-HR-1108-1920-139486]; European Regional Development Fund [KK.01.1.1.02.0016]

    Thin films made of weak polyelectrolytes poly-(allylamine hydrochloride) (PAH) and poly(acrylic acid) (PAA) have been fabricated on silicon wafers using the layer-by-layer (LbL) method. To study the influence of counteranion type on the growth and properties of PAH/PAA multilayers, the nature of the supporting sodium salt was varied from cosmotropic to chaotropic anions (F-, Cl-, and ClO4-). Results of ellipsometry and AFM measurements indicate that the film thickness and surface roughness systematically increase on the order F- < Cl- < ClO4-. Furthermore, we found that the hydrophobicity of the PAH/PAA multilayer also follows the described trend when a polycation is the terminating layer. However, the heating of PAH/ PAA multilayers to 60 degrees C during the LbL assembly suppressed the influence of background anions on the multilayer formation and properties. On the basis of the obtained results, it could be concluded that thermal annealing induces changes at the polymer-air interface in the sense of reorientation and migration of polymer chains.
    View publication