    Wettability of DPPC Monolayers Deposited from the Titanium Dioxide-Chitosan-Hyaluronic Acid Subphases on Glass

    Year: 2019

    Journal: Colloid Interfac., Volume 3, 1-Jan

    Authors: Ladniak, Agata; Jurak, Malgorzata; Wiacek, Agnieszka Ewa

    Organizations: MINISTRY OF SCIENCE AND HIGHER EDUCATIONMinistry of Science and Higher Education, Poland [BS-M-03-002-18-D-01]

    Keywords: wettability; contact angle; monolayer; phospholipid DPPC; titanium dioxide; chitosan; hyaluronic acid

    The investigations were carried out to determine wettability of the 1,2-dipalmitoyl-sn-glycero-3-phosphocholine (DPPC) monolayers transferred from the liquid subphases containing chitosan (Ch), hyaluronic acid (HA), and/or titanium dioxide (TiO2) to a glass support by means of the Langmuir-Blodgett (LB) technique. For comparative purposes, the analysis of the plates surfaces emerged from the analogous subphases without the phospholipid film was also made. Characterization of the DPPC monolayers was based on the contact angle measurements using three test liquids (water, formamide, diiodomethane) and a simulated body fluid (SBF) solution in which the concentration of ions was close to that of human plasma. After deposition of the DPPC monolayers on the glass plates, a significant increase in the contact angles of all the probe liquids was observed compared to the plates pulled out from the given subphase without floating DPPC. The presence of phospholipid monolayer increased the hydrophobic character of the surface due to orientation of its molecules with hydrocarbon chains towards the air. In addition, the components of the subphase attached along with DPPC to the glass support modify the surface polarity. The largest changes were observed in the presence of TiO2.