Molecular design of thin film composite (TFC) hollow fiber membranes for isopropanol dehydration via pervaporation

High performance hollow fiber membranes consisting of a thinfilmcomposite (TFC) polyamide layer and a porous Torlon® polyamide-imide substrate have been fabricated via interfacial polymerization for pervaporation dehydration of isopropanol. The effects of substrate characteristics on the formation of the thin polyamide layer and the pervaporation performance are investigated. It is found that the resultant TFCmembranes show superior separation performance if the substrates have a fine surface pore size and desirable sub-structural morphology. The effects of amine monomers, i.e., m-phenylenediamine (MPD) and hyperbranched polyethyleneimine (HPEI), for interfacial polymerization with trimesoyl chloride (TMC) on separation performance are also compared. The TFCmembrane prepared from HPEI exhibits a higher pervaporation flux than that from MPD possibly due to the fact that the former has higher amine content than the latter. As a consequence, the polyamide selective layer of the former has a greater hydrophilicity than the latter. X-ray photoelectron spectroscopy (XPS) and contact angle measurements have confirmed the hypothesis. The molecular weight of HPEI also affects the pervaporation performance of the resultant TFC membranes. With the optimal interfacial polymerization conditions, the TFC membrane fabricated from HPEI with a molecular weight of 2 kg/mol shows the best separation factor of 624 with a flux of 1282 g/m2-h and a permeate water concentration of 99.1 wt% using a feed composition of 85/15 wt% IPA/water at 50 °C. After post methanol treatment, the flux can be enhanced to 1920 g/m2-h with a slightly decrease in permeate water concentration to 98.4 wt%. The mechanism of flux enhancement has been examined by slow beam positron annihilation spectroscopy (PAS). It is found that the removal of the excess amine from the TFC layer during the methanol treatment is the main cause.