    Tailoring the mechanical properties of starch-containing layer-by-layer films

    Year: 2012

    Journal: Colloids and Surfaces A: Physicochemical and Engineering Aspects, Volume 394, 20 January 2012, Pages 14–22, 20120618

    Authors: Erik Johansson a, Lars Wågberg a, b

    Last authors: Lars Wågberg

    Organizations: •a Division of Fibre Technology, School of Chemical Science and Engineering, KTH Royal Institute of Technology, Stockholm, SE-100 44 Stockholm, Sweden •b The Wallenberg Wood Science Centre, School of Chemical Science and Engineering, KTH Royal Institute of Technology, Stockholm, SE-100 44 Stockholm, Sweden

    Country: Sverige, Sweden

    The Young's modulus of layer-by-layer (LbL) films containing starch was determined using the recently developed SIEBIMM (strain-induced elastic buckling instability for mechanical measurements) technique. By using cationic starch (CS) in combination with anionic starch (AS), silica nanoparticles (SNP), and nanofibrillated cellulose (NFC), the mechanical properties of these sub-micrometer starch-containing LbL films could be tailored. At 50% relative humidity (RH), the Young's modulus of CS/AS, CS/SNP, and CS/NFC was 0.6 GPa, 0.9 GPa, and 1.8 GPa, respectively, in the 25–85-nm thickness range. As expected for these hygroscopic starch-containing LbL films, the mechanical properties depended on RH. At 0% RH, the Young's modulus was 2–4.5 times higher than at 50% RH. The LbL buildup on polydimethylsiloxane (PDMS) was studied in situ using quartz crystal microgravimetry with dissipation (QCM-D), and atomic force microscopy (AFM) was used to characterize the surface morphology and thickness of the films.