    Adjustment of Cell Adhesion on Polyurethane Structures via Control of the Hard/Soft Segment Ratio

    Year: 2020

    Journal: Macromol. Mater. Eng., Volume 305, MAY

    Authors: Lutzweiler, Gaetan; Barthes, Julien; Vrana, Nihal Engin; Rawiso, Michel; Louis, Benoit; Mayingi, Josselin; Carre, Albane; Drenckhan, Wiebke; Schaaf, Pierre

    Organizations: Institut Carnot MICA (project DiaArt); ERC Consolidator GrantEuropean Research Council (ERC) [819511 -METAFOAM]; Horizon 2020 PANBioRA [760921]; doctoral school of physics and physical chemistry of Strasbourg

    Keywords: hard segments; isocyanate index; phase separation; polyurethane; wharton's jelly mesenchymal stem cells

    Creating substrates with a similar composition that can either prevent or promote cell adhesion is still a challenging feat. Here, it is shown that a strikingly simple method of tuning the amount of hard segments or isocyanate index (NCOind) of a polyurethane (PU) film allows to modulate cell adhesiveness. PU films are synthesized with NCOind of 75, 100, 200, 300 and 400 corresponding to ratios of isocyanate to hydroxyl functions of 0.75, 1, 2, 3, 4, respectively. The adhesive capacity of NIH 3T3 fibroblasts (3T3) and Wharton's jelly mesenchymal stem cells (WJMSCs) are dependent on the NCOind. For NCOind below 300, no cell adhesion can be observed regardless of the cell type, whereas for NCOind of 300 and 400 cells adhere to the PU surface. WAXS and small angle X-ray scattering (SAXS) studies reveal that variations of NCOind allows to modulate the phase separation in PU films. Porod's law shows that for NCOind of 300 and 400, the hard-soft segment interface is sharp. Conversely, samples with smaller NCOind present diffuse interfaces. Hence, the morphology of the interface between hard and soft domains appears to be a critical feature that correlates with the adhesion capacity of cells.