    Crown ether-modified polyelectrolytes and their interactions with cations - A QCM study

    Journal: Appl. Surf. Sci. Adv., Volume 11, OCT

    Authors: Sahin, Sevil; van Weeren, Emma; Zuilhof, Han; de Smet, Louis C. P. M.

    Organizations: European Research Council [682444]

    Keywords: Polyelectrolyte multilayers; Crown ether; Bio-based polymer; Pectin; Ion selectivity

    In this study, the build-up of polyelectrolyte multilayers (PEMs) containing 15-crown-5 (CE) groups and their interactions with various cations were studied by using quartz crystal microbalance with dissipation monitoring (QCM-D). First, poly(allylamine hydrochloride) (PAH) was modified with 4'-carboxybenzo-CE via carbodiimide chemistry. CE was chosen as its complexes with Na+ and K+ are reported to be more stable compared to those with other cations. The resulting functionalized polyelectrolyte (PAHCE) and poly(4-styrene sulfonic acid) (PSS) were used in the layer-by-layer build-up of a multilayer onto gold-coated quartz resonators, enabling their characterization with QCM-D. Compared to (PAH/PSS)(4), (PAHCE/PSS)(4) resulted in slightly thicker layers based on Voigt (65 +/- 5 vs. 57 +/- 3 nm) and Sauerbrey (45 +/- 2 vs. 38 +/- 3 nm) modelling of the QCM-D data. The same trend was found for the optical, dry thickness, as obtained with ellipsometry (15 +/- 0.3 vs. 13 +/- 1 nm). Next, the QCM-D characteristics of these PEMs were monitored in situ when exposed to various aqueous salt solutions (LiCl, NaCl, KCl, CsCl, RbCl, and MgCl2). Starting from Cs+, the frequency change of the (PAHCE/PSS)(4) system upon changing to K+ and Na+ solutions was found to be asymptotic to 3 times larger than for (PAH/PSS)(4). With a polycation (PAHCE) as the outermost PEM layer, the salt-exchange behavior was less visible due to increased charge rejection of cations. Therefore, we also modified a bio-based polyanion, pectin with 4'-aminobenzo-CE and built (PAH/pectinCE)(4). Also in this case, the addition of CE increased the PEM layer thickness compared to (PAH/pectin)(4), both in a wet state (Sauerbrey modelling, 447 +/- 19 vs. 314 +/- 17 nm) and when dry (115 +/- 4 vs. 66 +/- 3 nm). Again, we observed the largest QCM-D responses for K+ and Na+ solutions (asymptotic to 6 and 12 times larger, respectively) compared to (PAH/pectin)(4). The effect of CE is more prominent in pectin-based PEMs due their relatively higher thickness. Given the large toolbox of available polyelectrolytes and ionophores, we anticipate that functionalized PEMs can facilitate the further development of ion separation applications.
    View publication