Authors: Schmode, Philip; Ohayon, David; Reichstein, Paul M.; Savva, Achilleas; Inal, Sahika; Thelakkat, Mukundan
A new generation of polythiophene-based poly electrolytes is reported to address fundamental issues in organic electrochemical transistors (OECTs). In such devices, the semiconductor must be able to transport and store ions and possess simultaneously a very high electronic mobility. For this, the ion-conducting 6-(thiophen-3-yl) hexane-l-sulfonate tetramethylammonium monomer (THS-TMA(+)) is copolymerized with the hole-conducting 3-hexylthiophene (3HT) to obtain copolymers, PTHS(-)TMA(+)-co-P3HT 1-3 with a gradient architecture. The copolymers having up to 50 mol % 3HT content are easily oxidizable and are crystalline. Consequently, for the copolymers, a higher stability in water is achieved, thus reducing the amount of cross-linker needed to stabilize the film. Furthermore, OECTs using copolymers with 75 and 50 mol % of PTHS(-)TMA(+) content exhibit 2-3 orders of magnitude higher ON/OFF ratio and an extremely lower threshold voltage (-0.15 V) compared to PTHS(-)TMA(+). Additionally, high volumetric capacitance (C* > 100 F/cm(3)) is achieved, indicating that the ion transport is not hampered by the hydrophobic 3HT up to SO mol %, for which a very high OECT hole mobility of 0.017 cm(2)/(V s) is also achieved. Thus, the concept of copolymerization to combine both ionic and electronic charge transport in an organic mixed conductor offers an elegant approach to obtain high-performance OECT materials.